Encapsulant for microactuator suspension

ABSTRACT

A microactuator used for selectively altering a position of a transducing head carried by a slider in a disc drive system with respect to a track of a rotatable disc having a plurality of concentric tracks. The microactuator is of the type comprising a piezoelectric element. A polymer coating encapsulates all exposed surfaces of the piezoelectric element.

BACKGROUND OF THE INVENTION

[0001] The present invention generally relates to a disc drive microactuator. More particularly, the invention relates to an encapsulant covering all exposed surfaces of a component wherein the component may be selected from the group consisting of the microactuator, slider, disc spacer, surface mount component on a printed circuit card assembly, or a ceramic component of a disc drive. The invention further relates to a microactuator driven by piezoelectric (lead-zirconate-titanate) crystals, the microactuator having improved cleanliness and decreased particle generation levels within the drive.

[0002] Disc drive systems include disc drive suspensions for supporting transducing heads over information tracks of a rotatable disc. Typically, suspensions include a load beam having a mounting region on a proximal end, a flexure on a distal end, a relatively rigid region adjacent to the flexure, and a spring region between the mounting region and the rigid region. An air bearing slider, which holds the transducing head, is supported by the flexure. Tile mounting region is typically attached to a base plate for mounting the load beam to an actuator arm. A motor, which is controlled by a servo control system, rotates the actuator arm to position the transducing head over the desired information tracks on the disc. This type of suspension is used with both magnetic and non-magnetic discs.

[0003] The density of concentric data tracks on magnetic discs continues to increase (i.e., the size of data tracks and radial spacing between data tracks are decreasing), requiring more precise radial positioning of the transducing head. Conventionally, head positioning is accomplished by operating an actuator arm with a large-scale actuation motor, such as a voice coil motor (VCM), to radially position the head on the slider at the end of the actuator arm. The large-scale motor lacks sufficient resolution to effectively accommodate high track density discs. Thus, a high resolution head positioning mechanism, or microactuator, is necessary to accommodate the more densely spaced tracks.

[0004] One design for high resolution head positioning involves employing a high resolution microactuator in addition to the conventional low resolution actuator motor, thereby effecting head positioning through dual stage actuation. Various microactuator designs have been considered to accomplish high resolution head positioning. These designs, however, all have shortcomings that limit the effectiveness of the microactuator. Many designs increas the complexity of designing and assembling the existing components of the disc drive, while other designs are unable to achieve the force and bandwidth necessary to accommodate rapid track access. Therefore, those prior designs do not present ideal microactuator solutions.

[0005] More recent microactuator designs employ electroactive elements to effect movement of the suspension with respect to the actuator arm, i.e. suspension level microactuators, or to effect movement of the flexure with respect to the suspension. In a suspension level microactuator, the electroactive elements generally include piezoelectric crystal dies attached between a head mounting block (or base plate) of the actuator arm and the head suspension. The piezoelectric elements are typically ceramic PZT crystals and are either single layer or multi-layer (ML) crystals.

[0006] In the field of hard disc drives, ceramic (hard) particles are a major source of damage to recording heads and the disc media, and the PZT crystals are a source of ceramic particles within the drive. In operation, voltage is applied to the PZT crystals to deform the element and thereby effect movement of the suspension with respect to the actuator arm. The voltage application to the piezoelectric element causes expansion and contraction of the PZT die, which causes ceramic particles to be ejected from the surfaces and edges of the element. The particles are a potential source of damage to the recording head and disc media and result in hard errors, head failures, and loss of data.

[0007] Cleaning has been the primary method for hard particle removal, but cleaning weakens the grain boundaries and allows for more particles to be freed from the PZT crystal, thereby exasperating the hard particle problem. Multi-layer PZT crystals also pose an additional problem because moisture in the drive environment will cause electrode migration of the Ag—Pd electroding, which can significantly lower the insulation resistance of the ML PZT crystal. This effect will be observed as a loss in stroke performance of the head gimbal assembly over time.

[0008] Some prior systems have tried to minimize particles by cleaning of the suspension assembly in an aqueous or solvent system, but have not succeeded because the particle reduction plateaus. Other systems use glob-top encapsulants to minimize particles, but such encapsulants are not useful in a drive environment due to contamination issues and microactuator stroke reduction. In addition, some moisture barrier techniques involve embedding the ends of the layered electrodes in the PZT, but this technique minimizes the effective area of the ML crystal, reduces total potential stroke for a given die size, and contributes more area for particle generation. A microactuator, for example, is needed which minimizes particles ejected from the PZT crystals during voltage application, significantly reduces surface particulate levels, and provides a moisture barrier that does not contribute to hard particle generation or lower the insulation resistance in capacitance.

BRIEF SUMMARY OF THE INVENTION

[0009] The present invention is directed to an encapsulant suitable for covering all exposed surfaces of a component. The component may be usable in a disc drive and may be selected from the group consisting of a microactuator, slider, disc spacer, surface mount components on a printed circuit card assembly, or ceramic components of the disc drive. The encapsulant may cover a microactuator for selectively altering a position of a transducing head carried by a slider in a disc drive system with respect to a track of a rotatable disc having a plurality of concentric tracks. The microactuator may be of the type comprising a piezoelectric element. A polymer coating encapsulates all exposed surfaces of the piezoelectric element.

BRIEF DESCRIPTION OF THE DRAWINGS

[0010]FIG. 1 is a top view of a disc drive actuation system for positioning a slider over tracks of a disc.

[0011]FIG. 2 is a top view of a microactuation system for use in a dual stage disc drive actuation system for high resolution positioning of a slider.

[0012]FIG. 3 is cross sectional view of piezoelectric elements of the microactuator taken along line 3-3 of FIG. 2.

DETAILED DESCRIPTION

[0013]FIG. 1 is a top view of a disc drive actuation system 10 for positioning a slider 12 over a track 14 of a disc 16. Actuation system 10 includes voice coil motor (VCM) 18 arranged to actuate an actuator arm 20 on a spindle around an axis 22. A head suspension 24, or load beam, is connected to actuator arm 20 at a head mounting block 26. A flexure 28, or gimbal, is connected to a distal end of head suspension 24, and supports slider 12. Slider 12 carries a transducing head (not shown) for reading and/or writing data on concentric tracks 14 of disc 16. Disc 16 rotates around an axis 30, so that windage is encountered by slider 12 to keep it aloft a small distance above the surface of disc 16.

[0014] VCM 18 is selectively operated to move actuator arm 20 around axis 22, thereby moving slider 12 between tracks 14 of disc 16. However, for disc drive systems with high track density, VCM 18 lacks sufficient resolution and frequency response to position the transducing head on slider 12 over a selected track 14 of disc 16. Thus, a higher resolution microactuation device is used to finely position slider 12, as shown in FIG. 2.

[0015]FIG. 2 is a top view of a microactuation system for use in a dual-stage disc drive actuation system for high resolution positioning of slider 12. In particular, FIG. 2 shows a suspension level microactuator 32. Head mounting block 26, or the base plate, is attached to a distal end of actuator arm 20 (not shown). Head suspension 24 is attached to head mounting block 26 by microactuator 32. A distal end 34 of head suspension 24 is attached to flexure 28 and applies a preload force to slider 12 at a load point to force slider 12 into close proximity with a surface of disc 16 when the disc drive is in operation. Slider 12 is attached to flexure 28 by a tongue at a distal end of flexure 28.

[0016] The microactuator 32 includes a compliant connection joint 36 for connecting head suspension 24 to head mounting block 26. Head mounting block 26, head suspension 24, and compliant joint 36 may be formed of a single sheet of material. In the embodiment shown in FIG. 2, compliant connection joint 36 is comprised of two beams located between head suspension 24 and head mounting block 26.

[0017] Microactuator 32 further includes piezoelectric elements 38 a and 38 b mounted to head mounting block 26 and head suspension 24, generally parallel to compliant joint 36. Piezoelectric elements 38 a and 38 b are deformable longitudinally in response to control signals, an applied voltage, across the elements. Expansion and contraction of piezoelectric elements 38 a and 38 b results in deformation of compliant joint 36, causing rotation of head suspension 24 and slider 12 with respect to head mounting block 26, and thereby effecting high resolution positioning of the transducing head carried by slider 12. Complementary expansion and contraction of piezoelectric elements 38 a and 38 b in the direction of arrows 40 and 42, respectively, generate force which causes elastic deformation of compliant joint 36, resulting in rotational rigid body movement of head suspension 24 around joint 36 in the direction of arrow 44.

[0018] Piezoelectric elements 38 a and 38 b are generally comprised of PZT (lead-zirconate-titanate) crystal dies having a single layer of poly-crystal material or a multi-layer (ML) comprised of multiple, thin layers of poly-crystal material with electroding between each layer.

[0019] Also shown in FIG. 2 is a printed circuit card assembly (“PCCA”) 43, which operates as an additional component in the disc drive. Trace 45 electrically connects the slider to PCCA 43. The microactuation system includes several components, including ceramic components, such as slider 12 and disc spacers, and stainless steel components, such as head mounting block 26, head suspension 24, flexure 28, or actuator arm 20.

[0020]FIG. 3 is cross sectional view of microactuator 32 taken along line 3-3 of FIG. 2. Each piezoelectric element 38 a, 38 b of the microactuation system has a top surface 46 and a bottom surface 48, with bottom surface 48 being attached to head suspension 24 and head mounting block 26 by a conductive epoxy 49. Both top and bottom surfaces 46, 48 include an electrode 50 a and 50 b (typically gold), to provide an electrical interconnect between the disc drive and head suspension 24. Top electrodes 50 a provide an electrical connection to apply voltage to piezoelectric elements 38 a, 38 b and actuate head suspension 24.

[0021] During operation of microactuator 32, voltage is applied to piezoelectric elements 38 a and 38 b to cause expansion and contraction of the PZT crystal dies, which results in the ejection of ceramic hard particles from the hard surfaces and edges of the PZT dies. The ejected particles are a major source of damage to recording heads and disc media, and result in hard errors, head failures and loss of data. The present invention is an encapsulant covering all exposed surfaces of piezoelectric elements 38 a and 38 b within the microactuation system to prevent particle generation during operation of microactuator 32. The encapsulant also serves as a moisture barrier for ML PZT die by preventing water vapor from reaching the electrodes and causing corrosion of the electrodes.

[0022] As shown in FIG. 3, an encapsulant 52, or polymer coating, covers all exposed surfaces of piezoelectric elements 38 a, 38 b (i.e., all surfaces except bottom surface 48) attached to head suspension 24 and head mounting block 26. Polymer coating 52 is preferably applied to piezoelectric elements 38 a, 38 b prior to placement of piezoelectric elements 38 a, 38 b within the suspension assembly. Encapsulant 52 may be applied to piezoelectric elements 38 a, 38 b using various coating techniques, such as, but not limited to, dip or gravity flow coating, spray coating, spin coating, screen coating, roll coating, or vapor deposition. After coating piezoelectric elements 38 a, 38 b, polymer coating 52 is generally cured to facilitate cross linking of the polymer. Subsequent curing depends on the type of the polymer used, but usually consists of various curing techniques, such as, but not limited to heat, ultra-violet, or electron beam. Cross linking the polymer inhibits encapsulant 52 from becoming mobile during actuation and thereby restricts particles on the surface of elements 38 a, 38 b from becoming mobile. Once polymer coating 52 is fully cured, measured particles on the surface of elements 38 a, 38 b are reduced and the encapsulant acts as a moisture barrier to prevent corrosion of electrodes 50 a, 50 b. The polymer of encapsulant 52 has a minimal elastic constant such that it does not restrict motion of piezoelectric elements 38 a, 38 b and is electrically non-conductive.

[0023] Encapsulant 52 has a thickness of one micron or less so as to not restrict the motion of piezoelectric elements 38 a, 38 b or inhibit electrical connection to top electrode 50 a via soldering. More preferably, the thickness of encapsulant 52 is between 25 and 30 angstroms. The thin coating does not affect performance of piezoelectric elements 38 a, 38 b, (e.g., stroke performance or electrical performance). Furthermore, coating 52 is thin enough so that an electrical connection may be made to top electrode 50 a by soldering without degrading the surrounding encapsulant and/or requiring laser ablation.

[0024] Encapsulant 52 is comprised of a polymer coating such as a fluorocarbon polymer, parylene, or an epoxy. More preferably, the polymer is a fluoroacrylate or perfluoropolyether, such as EGC-1700® or Fomblin Z-Tetraol® (manufactured by Ausimont of Italy).

[0025] One example of polymer coating 52 is Tetraol®, or other fluoroacrylates or perfluoropolyethers. The fluoropolymers are generally applied to piezoelectric elements 38 a, 38 b with one of several coating processes, such as dip or gravity flow coating, spray coating or spring coating, to achieve a thin uniform coating. Polymer coating 52 has a thickness between 10 to 100 angstroms, depending upon the concentration of the coating solution and the method of coating used.

[0026] Curing crosslinks the polymer chains to provide a more robust and adhered coating. Curing can take the form of either heat, ultra-violet, or electron beam, depending upon the polymer used. However, the most preferred method of curing for fluoropolymers is electron beam. In the electron beam cure process, electrons are distributed uniformly throughout the coating with energies that can extend to several kilo electron volts (keV), which are much higher energies than the ultra-violet process. An electron beam vacuum cure has energies between 20,000 and 80,000 micro Coulombs per centimeter squared (μC/cm²) and an electron beam air or nitrogen cure has energies between 80,000 and 250,000 kilo Grays (kGry).

[0027] With fluoropolymers, uniformity of coating is achieved at 20 or more angstroms to allow for reduced liquid particle counts (LPC), minimized particle generation, and reduced degradation in ML PZT crystal stroke from water vapor penetration. In addition, fluoropolymers encapsulants can be soldered through to provide an electrical connection to the piezoelectric element.

[0028] A further example of polymer coating 52 is a parylene polymer applied using vapor deposition. The parylene is coated at a thickness between 0.5 microns and 1 micron, such that significant reduction in liquid particle counts are observed and no reduction in insulation resistance is monitored from lifetime testing of ML PZT crystals. Electrical bonding to the piezoelectric element is achieved by maintaining a thin parylene coating or by selectively removing the parylene by abrasion or laser ablation. Parylene coatings reduce the amount of particles extracted from the PZT crystal during liquid particle count. Parylene is also an effective moisture barrier and prevents water vapor from reaching the electrodes, which would cause dendritic growth of the electrodes and corrosion under applied voltage.

[0029] Another example of polymer coating 52 used in the present invention is epoxy polymers. Epoxy is applied with one of several coating processes, such as, dip or gravity flow coating, spray coating, spin coating, or roll coating, to achieve a thin uniform coating. The epoxy coating is cured thermally at various temperatures.

[0030] The present invention includes a polymer coating encapsulant covering all exposed surfaces of a piezoelectric element of a microactuation system. The polymer coating provides a moisture barrier to prevent water vapor from reaching the electrodes of the piezoelectric element, which would cause dendritic growth of the electrodes, corrosion under applied voltage, and lower insulation resistance capacitance. In addition, the encapsulant as a moisture barrier does not contribute to hard particle generation. The present invention encapsulant allows for free movement of the PZT crystal, in addition to locking particles at the piezoelectric surface. Furthermore, the polymer coating reduces the amount of particles extracted during liquid particle counts and during voltage application to the piezoelectric element (i.e., the liquid particle counts and aerosol particle counts are lowered and the particle generation from the piezoelectric elements is minimized). The present invention is a cost effective way of reducing contamination in the disc drive for microactuator components because the application and curing of the encapsulant can be preformed inline during manufacture of the piezoelectric elements. Furthermore, the present invention is a unique way to prolong the product life of ML PZT in the disc drive environment because of the moisture barrier capabilities.

[0031] The present invention encapsulant is also effective as a polymer coating for other components of the disc drive assembly to prevent hard particle generation within the disc drive. The encapsulant covers all exposed surfaces of components of the disc drive, such as the microactuator, the slider, a disc spacer, surface mount components on a printed circuit card assembly, any ceramic component of the disc drive assembly or any stainless steel component of the disc drive assembly, such as the head mounting block, load arm assembly, flexure or actuator arm.

[0032] Although the present invention has been described with reference to preferred embodiments, workers skilled in the art will recognize that changes may be made in form and detail without departing from the spirit and scope of the invention. 

1. An improved disc drive for positioning a slider carrying a transducing head with respect to a selected track of a rotatable recording disc, the disc drive of the type having a movable actuator arm, a head suspension, a microactuator, a flexure, a slider and a transducing head carried by the slider, the improvement comprising: an encapsulant covering all exposed surfaces of a component selected from the group consisting of the microactuator, the slider, a disc spacer, surface mount components on a printed circuit card assembly, ceramic components of the disc drive, and stainless steel components of the disc drive.
 2. The improvement of claim 1, wherein the encapsulant is selected from the group consisting of a fluorocarbon polymer, parylene, and an epoxy.
 3. The improvement of claim 1 wherein the encapsulant has a thickness of one micron or less.
 4. An improved microactuator for selectively altering a position of a transducing head carried by a slider in a disc drive system with respect to a track of a rotatable disc having a plurality of concentric tracks, the microactuator of the type including a piezoelectric element, the improvement comprising: a polymer coating encapsulating all exposed surfaces of the piezoelectric element.
 5. The improvement of claim 4 wherein the polymer coating is applied to the piezoelectric element prior to placement of the piezoelectric element in the disc drive system.
 6. The improvement of claim 4 wherein the polymer coating is applied to the piezoelectric element by dip coating, gravity coating, spray coating, screen coating, roll coating or vapor deposition.
 7. The improvement of claim 6 wherein after the polymer coating is applied to the piezoelectric element, the piezoelectric element is cured by heat, ultra-violet rays or an electron beam.
 8. The improvement of claim 4 wherein the polymer coating is substantially uniform.
 9. The improvement of claim 4 wherein the polymer coating has a thickness of one micron or less.
 10. The improvement of claim 9 wherein the thickness of the polymer coating is between about 25 angstroms and about 30 angstroms.
 11. The improvement of claim 4 wherein the polymer coating is selected from the group consisting of a fluorocarbon polymer, parylene and an epoxy.
 12. A microactuator comprising: a first piezoelectric element attached between a mounting block and a suspension, the first piezoelectric element being deformable in response to a voltage applied thereto; a uniform polymer coating encapsulating all exposed surfaces of the first piezoelectric element; and a compliant joint connected between the mounting block and the suspension, the compliant joint being flexible to permit movement of the suspension with respect to the mounting block.
 13. The microactuator of claim 12 wherein the first piezoelectric element is comprised of a single layer crystal die.
 14. The microactuator of claim 12 wherein the first piezoelectric element is comprised of a multiple layer crystal die.
 15. The microactuator of claim 12 wherein the first polymer coating is selected from the group consisting of a fluoroacrylate, a perfluoropolyether, an epoxy, and parylene.
 16. The microactuator of claim 12 wherein the polymer coating has a thickness of one micron or less.
 17. The microactuator of claim 12, and further comprising a second piezoelectric element attached between the mounting block and the suspension, the second piezoelectric element being encapsulated by a uniform polymer coating and deformable in a direction complementary to deformation of the first piezoelectric element in response to a voltage applied thereto. 